Characterization of the flexural behavior of a reactive graphitic nanofibers reinforced epoxy using a non-linear damage model

In our previous work, a nano-epoxy was developed based on the preparation of reactive graphitic nanofibers (r-GNFs). The objective of this work is to study the effect of the r-GNFs in an epoxy resin on the mechanical properties of the resulting nano-epoxy composites. Three-point bending tests were carried out for the pure epoxy and nano-epoxy materials with 0.15, 0.2, 0.3, 0.5 wt% r-GNFs to obtain the flexural behaviors. The nano-epoxy composite containing 0.3 wt% of r-GNFs showed the best flexural properties including highest flexural strength, modules and ductility values among all the tested materials. Non-linear fracture mechanics (NLFM) was applied to analyze the phenomena occurred during the bending tests. A non-linear damage model was used to interpret the flexural stress–strain relationships of the tested materials, which showed agreement with the testing results. The fracture surfaces of the nano-epoxy composites were examined with scanning electron microscopy (SEM), and the morphological features on the SEM images also reveals that the nano-epoxy composites are tougher than the pure epoxy resin.