Zr-rich Zr–Ti–Ni(Cu) alloy system with deep eutectics was investigated for bulk metallic glass (BMG) compositions. The BMGs were investigated by locating deep eutectic compositions and by evaluation of alloys near it. When Cu was added to the Zr45Ti21Ni34 eutectic alloy as an additional melting point depressant, even lower melting eutectics were obtained. A new quaternary eutectic alloy was found with a composition of Zr49Ti17Ni20Cu14. The microstructure consists of three glass forming compounds of Zr2Ni, Zr2Cu, and (Zr,Ti)2Ni. By examining alloys around the new quaternary eutectic alloy, a BMG with a glass forming ability of 4 mm diameter was found at the off-eutectic Zr49Ti14Ni20Cu17 composition. The study confirmed the composition of the best glass former near the eutectic point. The searching method for BMGs starting from a deep eutectic alloy as a reference point is described.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Exploration of a deep eutectic point by adding Cu in the Zr-Ti-Ni alloy. ► A true eutectic point at Zr49Ti17Ni20Cu14composed of three intemetallic phases. ► Search for bulk metallic glasses near the eutectic point. ► Successful formation of bulk metallic glass of 4 mm-diameter at the Zr49Ti14Ni20Cu17.