Preparation of WC nanoparticles by twice ball milling

•Twice ball milling was carried out in nylon vessels for WC nanoparticles.•PEG and La2O3 were added to improve the ball milling efficiency.•PEG can narrow the size distribution and La2O3 can reduce the particle size.

In order to improve the ball milling efficiency of WC powders and thus to fabricate nano-grained WC–Co cemented carbides with high mechanical properties, WC nanoparticles were prepared by twice ball milling in nylon vessels. The best technology to disperse WC powders in alcohol was investigated at first. Based on the dispersion results, 2 wt.% PEG was used with La2O3 as additive to improve ball milling efficiency. The particle size, crystal structure, surface morphology and surface properties were tested by a laser particle sizer, XRD, FE-SEM and FT-IR, respectively. During the first ball milling, sample d achieved the best milling performance, including average particle size (168 nm) and grain size (27.2 nm) among samples a (pure WC), b (with PEG), c (with La2O3) and d (with PEG and La2O3). La2O3 could greatly decrease particle size and grain size while PEG could narrow particle size distribution. During the second milling, the particle size and grain size of sample d reached 89 nm and 13.2 nm at 96 h, respectively. The results indicated that twice ball milling can greatly improve particle size and grain size compared with the first ball milling, and further narrow the size distribution. In conclusion, multiple ball milling can reduce the particle size of certain powders with suitable milling technology.