1608046 Journal of Alloys and Compounds 2015 7 Pages PDF
Abstract

•Average crystallite size of these ferrites is in the range of 34–44 nm.•Dielectric constant of the samples rises from 12.8 to 32.7 with Ta–K at 1.0 GHz.•Coericivity of the synthesized samples is greater than 600 Oe.

Tantalum–potassium substituted strontium calcium hexagonal ferrites with chemical composition Sr0.5Ca0.5Fe12-2xTaxKxO19 (x = 0.0, 0.1, 0.2, 0.3, 0.4) have been synthesized by the sol gel combustion procedure. The structural and morphological characterizations of the synthesized hexaferrites were performed by X-ray diffraction and scanning electron microscopy, respectively. Dielectric and magnetic properties of these samples were also inspected. XRD analysis revealed that all the prepared compounds have pure magnetoplumbite phase and their mean crystallite size was between 34 and 44 nm.The dielectric parameters present resonance type behavior at higher frequency (GHz) region. The dielectric constant increases as the dopant contents increase. The saturation magnetization and remanence show decreasing trend as the concentration of dopants rise in the range of applied magnetic field. The coericivity of all the prepared samples rises with Ta–K concentration and is high enough to be used for longitudinal magnetic recording media.

Graphical abstractComposition dependence of dielectric constant and dielectric loss of all the prepared samples at ambient temperature and 1.0 GHz.Figure optionsDownload full-size imageDownload as PowerPoint slide

Related Topics
Physical Sciences and Engineering Materials Science Metals and Alloys
Authors
, , , ,