Structural transformations in the Co53Mo35Cr12 alloy at different temperatures

Structural transformations of the Co53Mo35Cr12 alloy were studied at temperatures of 1250, 1000 and 700 °C, when in all the three diffusion couples of the alloy there takes place a tendency to phase separation and at a temperature above the solidus, when in the Co/Mo diffusion couple there appears a tendency to ordering and the Со3Мо phase is formed. It has been shown that at a temperature of 1250 °C, this phase is completely dissolved, and in the process of such dissolution, a Co-enriched fcc solid solution with a large number of stacking faults is formed. Simultaneously, there occurs precipitation of particles of Сr atoms, the sizes of which grow with lowering the temperature of heat treatment. The stacking faults, formed at 1250 °C, turn out to be the place, where laths enriched in Mo atoms, begin to form. After a heat treatment at 700 °C, the whole structure of the alloy consists of light-color and dark laths, arranged along the elastically- soft directions of the matrix. Each of these laths is enriched in atoms of either cobalt (fcc lattice) or molybdenum (bcc lattice).