Abstract
⺠Phase equilibria in the Al-Cr-Ti system were studied up to 75 at.% Al at 1473 K. ⺠Formation of a continuous solid solution in the β phase was confirmed. ⺠Extended homogeneity range of the Ï, γ-TiAl and (Al8Cr5)h phases were measured. ⺠Ternary extension of the C14 Laves phase was determined as 8.3 at.% Al.