In the present study, we have studied the exchange bias interaction in ferromagnetic Sr2FeMoO6 (SFMO)/antiferromagnetic Sr2FeWO6 (SFWO) multilayer thin films deposited on single crystal LaAlO3 substrates using KrF pulsed laser deposition technique. XRD pattern revealed that SFMO, SFWO and their multilayer thin films were highly oriented along the c-axis. The microstructure studied by atomic force microscopy was found to be uniform, fine, dense and homogenous in nature. The observed magnetization-temperature curves showed Neel temperature TN ∼ 37 K for SFWO and Curie temperature TC > 320 K for SFMO thin films. For multilayer, the field cooled magnetization–field curve was shifted horizontally and the direction of the horizontal shift is opposite to that of HFC, indicating an exchange bias effect. Exchange bias field HE was found to decrease with increase in temperature and approached to zero at blocking temperature.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideHighlights► SFMO is a ferromagnetic (FM) conductor with a high TC ∼ 420 K. ► SFWO is an anti-ferromagnetic (AFM) insulator with a low TN ∼ 37 K. ► Hysteresis loop for [SFMO/SFWO]15 after FC shifts horizontally opposite to the HFC. ► HE decreases with increase in temperature and approaches to zero above TB. ► HC decreases on either side of TB where it finds its maximum value.