In this study the influence of two different calcination temperatures 80 °C and 450 °C on the structural, optical and charge transport properties of rutile TiO2 nanocrystals has been investigated. TiO2 nanocrystals have been prepared at low temperature by a simple hydrolysis method using titanium tetrachloride as starting precursor. The results of X-ray diffraction (XRD) showed that the prepared nanocrystals have a rutile tetragonal crystalline structure. Specific surface area of 80 °C and 450 °C calcinated rutile TiO2 nanocrystals are 25.38 × 105 cm2/g and 7.61 × 105 cm2/g respectively, which has been calculated by X-ray diffraction data. Williamson–Hall plot results indicate the presence of compressive strain at 80 °C and tensile strain at 450 °C. Ultraviolet–visible (UV–vis) absorption spectroscopy is used to calculate the band gap of the material and the shift in absorption edge and it has been observed that the absorption spectra are strongly modified by the calcination temperature. The red-shift in photoluminescence (PL) is attributed to the change in strain from compressive to tensile. Photoconductivity (PC) measurements showed that capture cross-section of 80 °C (R1) and 450 °C (R2) calcinated rutile nanocrystals are 55.10 × 10−10 and 39.50 × 10−10 cm2 respectively. High value of electron life-time, low value of radiative recombination and a four order increase in photogenerated charge carriers have been reported for the rutile TiO2 nanocrystals calcinated at 450 °C.
Graphical abstractIn this study an attention has been drawn to the advantages to be derived from a comparative analysis of structural, optical and charge transport properties of the rutile TiO2 at two different calcination temperatures of 80 °C and 450 °C.Figure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Investigation of structural properties of rutile TiO2 at two calcination temperature. ► Comparison of densities, lattice spacing and surface areas of rutile TiO2. ► Study of effect of calcination temperature on optical properties of rutile TiO2. ► Comparative study of charge transport properties at two temperatures.