Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1617333 | Journal of Alloys and Compounds | 2011 | 4 Pages |
Abstract
⺠Nanopowders of Fe0.54Cr0.18Al0.26Si0.016 and Al2O3 were fabricated from Fe2O3, Cr, Si, and Al powders using high-energy ball milling. ⺠Densification of a nanostructured 3.7Fe0.54Cr0.18Al0.26Si0.016-Al2O3 composite prepared from mechanically alloyed powders was accomplished using the PCASM. ⺠Complete densification was achieved within a processing time of 3 min under an applied pressure of 80 MPa and an induced current. ⺠The average grain sizes of the Fe0.54Cr0.18Al0.26Si0.016 alloy and Al2O3 prepared through PCASM were approximately 22 nm and 48 nm, respectively, and the average hardness value was 450 kg/mm2.
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
In-Jin Shon, Seung-Hoon Jo, In-Yong Ko, Jung-Mann Doh, Jin-Kook Yoon, Sang-Whan Park,