Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1619315 | Journal of Alloys and Compounds | 2010 | 6 Pages |
Interactions between LiAlH4 and LiNH2 through a gaseous ammonia intermediate have been investigated. LiAlH4 and LiNH2 powders with a molar ratio of 1:1 were separated in two containers inside a reactor and heated from room temperature to 350 °C at a heating rate of 1 °C/min. The results showed that LiNH2 would decompose into Li2NH and NH3 to certain extent even at a relatively low temperature. Ammonia then reacted with Al and LiH that decomposed from LiAlH4, whereupon the chemical equilibrium of the system was altered and the initial reaction temperature was lowered. Ammonia decomposed from LiNH2 acted as an intermediate. A pathway for the thermal decomposition of the system was proposed as:LiNH2+LiAlH4→8−3m10Li2NH+2+3m5LiH+2+3m10AlN+8−3m10Al+48−3m20H2 (0