The new BIMEVOX series of Bi4HfxV2−xO11−(x/2)−δ; 0 ≤ x ≤ 0.40 was synthesized by solid state reactions. Structural phase transitions as a function of composition were investigated by FT-IR, X-ray powder diffraction, differential scanning calorimetry and Arrhenius plots of conductivity. Two consecutive phase transitions, α ↔ β ↔ γ, were well characterized for x = 0.05 composition. The existence of β ↔ γ transition was clearly evident for relatively higher compositions 0.15 ≤ x ≤ 0.20 which is typified to two line regions of different activation energy on the Arrhenius plots. However, the existence of only γ′ ↔ γ transition was clearly confirmed for high compositions 0.25 ≤ x ≤ 0.40. AC impedance analysis also showed that the ionic conductivity is mainly due to the grain contribution which is clearly pronounced by the short-range diffusibility of oxide ion vacancies within the grains. The composition dependence of conductivity exhibited significant maximum in low temperature region (σ340 = 7.31 × 10−5 S cm−1) for x = 0.25 composition.

Related Topics
Physical Sciences and Engineering Materials Science Metals and Alloys
Authors
, , ,