Effects of benzotriazole on anodized film formed on AZ31B magnesium alloy in environmental-friendly electrolyte

An environmental-friendly electrolyte of silicate and borate, which contained an addition agent of 1H-benzotriazole (BTA) with low toxicity (LD50 of 965 mg/kg), was used to prepare an anodized film on AZ31B magnesium alloy under the constant current density of 1.5 A/dm2 at room temperature. Effects of BTA on the properties of the anodized film were studied by scanning electron microscopy (SEM), energy dispersion spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), loss weight measurement, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS), respectively. The results demonstrated that anodized growth process, surface morphology, thickness, phase structure and corrosion resistance of the anodized film were strongly dependant on the BTA concentration, which might be attributed to the formation of an BTA adsorption layer on magnesium substrate surface. When the BTA concentration was 5 g/L in the electrolyte, a compact and thick anodized film could provide excellent corrosion resistance for AZ31B magnesium alloy.