VC- and Cr3C2-doped WC–NbC–Co hardmetals

This study compares the microstructure and mechanical properties of plain and 0.9 or 3.6 wt% VC- or Cr3C2-doped WC–12 wt% Co hardmetals with 40 wt% NbC, prepared by pulsed electric current sintering (PECS) in the solid state for 4 min at 1240 °C and conventional pressureless liquid phase sintering (CS) for 1 h at 1420 °C. The addition of VC or Cr3C2 was found to inhibit grain growth of the residual WC grains, whereas the size of the solid solution (Nb,W,V/Cr)C grains was hardly influenced. The type of grain growth inhibitor and densification temperature however, strongly influenced the composition of the NbC solid solution formed, which was thermodynamically and experimentally assessed.