Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1623878 | Journal of Alloys and Compounds | 2008 | 4 Pages |
Abstract
CuZr phase is precipitated easily in the process of fabricating Zr50.5Cu34.5Ni4Al11 BMG. The critical diameter of amorphous rod is improved from 8Â mm of Zr50.5Cu34.5Ni4Al11 to at least 20Â mm of Zr53.5Cu26.5Ni5Al12Ag3 by restraining the precipitation of CuZr phase. The great improvement of GFA is attributed to the declination of Cu content and the weakening of the drastic interaction between Cu and Zr atoms by Ag addition since Ag has similarly physical and chemical properties with Cu. Therefore, suppressing the precipitation of crystalline phase should be an effective method to enhance GFA.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys