The amorphous Fe81Nb5B14 alloys were obtained by melt spinning method as ribbons of 10 mm width and 25 μm thickness. For the creation of the nanocrystalline structure the alloys were annealed at the temperature range of 300–1025 K. The amorphous state was observed till temperature of 730 K. After annealing at 760 K the creation of the nanocrystalline solid solution based on α-Fe structure was observed. The full crystallisation of α-Fe and borides (Fe2B and Fe3B) was observed after annealing at temperature of 1025 K.The amorphous alloys were analysed by the Radial Distribution Functions in case of the coordination radii calculation. The analysis has shown that the basic type of order is typical for α-Fe model structure.Both, the amorphous and the nanocrystalline alloys were analysed by the Rietveld refinement.