Abstract
The relationship between the microstructure transformation of type 17-4 PH stainless steel and the aging hardening behavior was investigated. The results showed that, when 17-4 PH stainless steel aging at 595°C, the bulk hardness of samples attains its peak value (42.5 HRC) for about 20 min, and then decreases at all time. TEM revealed the microstructure corresponding with peak hardness is that the fine spheroid-shape copper with the fee crystal structure and the fiber-shape secondary carbide M23C6 precipitated from the lath martensite matrix. Both precipitations of copper and M23C6 are the reasons for strengthening of the alloy at this temperature. With the extension of holding time at this temperature, the copper and secondary carbide grow and lose the coherent relationship with the matrix, so the bulk hardness of samples decreases.
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Jun Wang, Hong Zou, Cong Li, Ruling Zuo, Shaoyu Qiu, Baoluo Shen,