Tribological Properties of SiNx Films on PH Stainless Steel with and Without Nitriding as a Pre-treatment

In this work, the tribological behavior and adhesion of SiNx films deposited by PACVD on nitrided and non-nitrided Corraẍ PH stainless steel were evaluated. The films were characterized by FTIR and EDS, hardness was assessed with a nanoindenter and the microstructure was analyzed by Optical Microscopy, SEM and FIB. To evaluate the tribological behavior, fretting and linear sliding tests were performed using WC and alumina balls as counterparts, and the adhesion of the SiNx films was characterized using the Scratch Test and Rockwell C indentation methods. Erosion tests were conducted in sea water and sand flux. Corrosion behavior was evaluated by the Salt Spray Fog Test. The film reached a hardness of 2300 HV and a thickness of about 1.4 microns. The duplex coated sample had a better tribological behavior than the simple coated sample, the nitrided layer allowed a graded interlayer which improved the wear resistance. Regarding the film adhesion, the duplex coating had an acceptable adhesion; the nitrided layer reduced the interface stress and enhanced the adhesion. Additionally, the films evidenced good corrosion resistance in a saline environment.