Synthesis of ZSM-5 zeolite membranes without organic templates using a varying-concentration technique

Template-free nanosized ZSM-5 seeds with an average size of 15 nm were prepared from a synthesis solution with the composition 12Na2O:100SiO2: 2Al2O3:2500H2O. By the use of these seeds, thin ZSM-5 zeolite membranes were prepared on the outer surface of a porous α-alumina tube with a pore size of 2 μm in a gel system by varying-concentration synthesis with organic-free template. The first composition synthesis sol-gel was the same as seeds of molar composition and the second one was 12Na2O: 100SiO2: 2Al2O3: 5000H2O at 180 °C for 10 h, respectively. XRD shows that the film consists of well-crystallized ZSM-5 zeolite. SEM investigation indicats that the zeolite films on the supports are defect free and the film thickness is approximately 8 μm. The permeances for H2, N2, CH4 and CO2 are 8.94 × 10−7, 3.27 × 10−7, 3.9 × 10−7, 3.14 × 10−7 and 0.874 × 10−7 mol·m2·s−1·Pa−1, respectively. The ideal selectivity of membrane at room temperature for H2/CO2, H2/N2, H2/CH4 are 2.84, 2.73 and 2.29, respectively.