Abstract
The influence of Li addition on mechanical property and aging precipitation behavior of Al-3.5Cu-1.5Mg alloy was investigated by tensile test, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The results show that the tensile strength can be significantly improved with the slightly decreased ductility and the form of fracture morphology is converted from ductile fracture into ductile/brittle mixed fracture by adding 1.0% Li. Besides, the peak aging time at 185 °C is delayed from 12 to 24 h and the main precipitation phase S'(Al2CuMg) is converted into S' (Al2CuMg)+δ'(Al3Li), while the formation of S'(Al2CuMg) is delayed.