Abstract
Ti-Al complex with a network microstructure was successfully fabricated by pressure infiltration. The fabricated Ti-Al complex was investigated and analyzed by OM, XRD, SEM and EDS. The temperature of pressure infiltration was reduced by using Al-Si eutectic alloy instead of pure Al, which can effectively decrease non-diffusion reaction between liquid Al and solid Ti particles. The reaction thickness can be controlled at about 3 μm. The primary reaction product is TiAl3 intermetallics. As Ti atoms dissolve into the Al-Si liquid phase and Si atoms enrich on the surface of Ti particles, TiSi2Al is formed in Al phase of Ti-Al complex and outside the surface of Ti-Al reaction layer. The microstructure of the as-extruded Ti-Al complex indicates that the prepared Ti-Al complex possesses a superior deformation capability.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Ce LIANG, Feng LI, Lin GENG, Lu-jun HUANG,