The microstructure of semi-solid isothermal heat-treated AZ61-0.7Si magnesium alloy was investigated, and compared with that of the Sb-modified AZ61-0.7Si alloy. The results indicate that it is possible to produce the AZ61-0.7Si alloy with a non-dendritic microstructure by semi-solid isothermal heat treatment, and adding 0.4% Sb can accelerate the non-dendritic microstructural evolution of the alloy. After being treated at 580 °C for 120 min, the Sb-modified AZ61-0.7Si alloys can obtain a non-dendritic microstructure with a higher liquid content (16%–18%) and finer unmelted primary solid particles (43–53 μm) compared with the alloy without Sb modification. In addition, after being treated at 580 °C for 120 min, the Mg2Si phases in the AZ61-0.7Si alloys with and without Sb modification change from initial Chinese script shape to granule and/or polygon shapes.