The effects of thin film nucleation and initial growth on roughness, chemistry and thermomechanical properties of polymer film surfaces were studied. Al2O3 was deposited onto commercial biaxially oriented polypropylene and polylactic acid films at 80 °C by using atomic layer deposition technique. Both substrates, especially the more hydrophobic polypropylene, showed initial growth through Al2O3 clusters. There was a faster deposition of Al2O3 on polylactic acid film than on polypropylene at the early stages of the Al2O3 deposition. There were also indications of chemical interactions between polylactic acid and trimethyl aluminum used as a precursor for Al2O3. Changes in the thermo-mechanical properties of the polymer surfaces with Al2O3 also evidenced the differences between the substrate polymer films. The near surface interphase formed in polylactic acid probably contributed to the strong increase and scattering in the softening temperature during the early thin film growth.
► Growth of atomic layer deposited Al2O3 at 80 °C was studied on commercial films. ► Both substrate films showed early Al2O3 growth through clusters. ► Initial growth rate depends on the nature of the substrate film surface. ► There were indications of chemical interactions between substrate and precursor. ► Film thickness and chemical interactions affect thermo-mechanical properties.