Influence of 150Â MeV Ni11+ swift heavy ion irradiation on CuFe2O4 thin films prepared by radio frequency magnetron sputtering: Modification on structure and surface morphology

The bulk copper ferrite nanomaterials are synthesized by co-precipitation technique. The vibrating sample magnetometer measurement for bulk CuFe2O4 reveals its unsaturated superparamagnetic behavior. The crystallites of the synthesized nanomaterial are in cubic form having an average size of ~ 100 Å and are used as target to prepare thin films of various thicknesses (600, 900 and 1100 nm) by radio frequency magnetron sputtering technique. X-ray peaks arise only when films are annealed at 1200 °C and also they are found to be in tetragonal structure. The magnetic characteristics of 900 nm unirradiated CuFe2O4 thin film exhibit superparamagnetic behavior and have an unsaturated magnetic moment at high field. Magnetic force microscopy images of unirradiated CuFe2O4 thin films confirm the soft nature of the magnetic materials. The 150 MeV Ni11+ swift heavy ion irradiation on these thin films at the fluence of 1 × 1014 ions/cm2 modifies the polycrystalline nature due to electron-phonon coupling. Atomic force microscopy image shows that the swift heavy ion irradiation induces agglomeration of particles in 600 and 900 nm thin films and increases rms surface roughness from 33.43 to 39.65 and 69.7 to 102.46 nm respectively. However, in 1100 nm film, holes are created and channel-like structures are observed along with a decrease in the rms surface roughness from 75.12 to 24.46 nm. Magnetic force microscopy images of 900 nm irradiated thin film explain the formation of domains on irradiation and are also supported by the ferromagnetic hysteresis observed using vibrating sample magnetometer.