Structural and dielectric properties of (001) and (111)-oriented BaZr0.2Ti0.8O3 epitaxial thin films

We have grown and characterized BaZr0.2Ti0.8O3 (BZT) epitaxial thin films deposited on (001) and (111)-oriented SrRuO3-buffered SrTiO3 substrates by pulsed laser deposition. Structural and morphological characterizations were performed using X-ray diffractometry and atomic force microscopy, respectively. A cube-on-cube epitaxial relationship was ascertained from the θ–2θ and φ diffractograms in both (001) and (111)-oriented films. The (001)-oriented films showed a smooth granular morphology, whereas the faceted pyramid-like crystallites of the (111)-oriented films led to a rough surface. The dielectric response of BZT at room temperature was measured along the growth direction. The films were found to be ferroelectric, although a well-saturated hysteresis loop was obtained only for the (001)-oriented films. High leakage currents were observed for the (111) orientation, likely associated to charge transport along the boundaries of its crystallites. The remanent polarization, coercive field, dielectric constant, and relative change of dielectric permittivity (tunability) of (111)-oriented BZT were higher than those of (001)-oriented BZT.