The photoluminescent (PL) and electroluminescent (EL) characteristics in the thin films of various Bi-activated binary oxide phosphors have been investigated. La2O3:Bi, Gd2O3:Bi and Y2O3:Bi phosphor thin films were prepared on thick BaTiO3 ceramic sheet substrates by r.f. magnetron sputtering depositions followed by postannealing. Intense blue PL emissions were observed from all Bi-activated binary oxide phosphor thin films postannealed at a high temperature. Blue, whitish blue-green or blue-green emissions were observed from thin-film electroluminescent (TFEL) devices fabricated with a La2O3:Bi, a Gd2O3:Bi or a Y2O3:Bi thin-film emitting layer, respectively. In addition, high luminance with good color purity in blue EL was obtained in a TFEL device using a La2O3:Bi thin film prepared under optimized conditions.