Phase separated AlSi thin films prepared by filtered cathodic arc deposition

Phase separated AlSi films composed of Al cylinders embedded in an amorphous Si matrix were prepared on conducting Si substrates by filtered cathodic arc deposition. The compositional dependence of AlSi films on a negative substrate bias showed a different trend depending on the cathode composition because of the self-sputtering process during the deposition. The porous structure was obtained from the phase separated AlSi film after removal of Al cylinders by wet etching in an ammonia solution. Scanning electron microscope images of the etched AlSi films showed that the average diameter of pores was increased from 3 nm to 7 nm by applying a negative substrate bias voltage during the deposition. The honeycomb ordered arrangement of pores was observed at 0 V and − 25 V substrate bias. The substrate temperature during the depositions had almost the same effect on the film morphologies as the negative substrate bias.