Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1680066 | Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms | 2015 | 6 Pages |
Amorphous silicon nitride films (thickness 30 nm) deposited on Si(0 0 1) were irradiated with 30–1080 keV C60 and 100 MeV Xe ions to fluences ranging from 2 × 1011 to 1 × 1014 ions/cm2. The composition depth profiles of the irradiated samples were measured using high-resolution Rutherford backscattering spectrometry. The sputtering yields were estimated from the derived composition profiles. Pronounced preferential sputtering of nitrogen was observed in the electronic energy loss regime. In addition, a large synergy effect between the electronic and collisional sputtering was also observed. The sputtering yields were calculated using the unified thermal spike model to understand the observed results. Although the calculated results reproduced the observed total sputtering yields with a lowered sublimation energy, the observed preferential sputtering of nitrogen could not be explained. The present results suggest an additional sputtering mechanism related to the electronic energy loss.