Temperature dependence of lattice disorder in Ar-irradiated (1 0 0), (1 1 0) and (1 1 1) MgO single crystals

To better appreciate dynamic annealing processes in ion irradiated MgO single crystals of three low-index crystallographic orientations, lattice damage variation with irradiation temperature was investigated. Irradiations were performed with 100 keV Ar ions to a fluence of 1 × 1015 Ar/cm2 in a temperature interval from −150 to 1100 °C. Rutherford backscattering spectroscopy combined with ion channeling was used to analyze lattice damage. Damage recovery with increasing irradiation temperature proceeded via two characteristic stages separated by 200 °C. Strong radiation damage anisotropy was observed at temperatures below 200 °C, with (1 1 0) MgO being the most radiation damage tolerant. Above 200 °C damage recovery was isotropic and almost complete recovery was reached at 1100 °C. We attributed this orientation dependence to a variation of dynamic annealing mechanisms with irradiation temperature.