Surface modification of SUS304 stainless steel by atmospheric pressure Ar/N2/O2 plasma

The surface characteristics of SUS304 stainless steel are investigated before and after surface modification by Ar/N2/O2 plasma under atmospheric pressure conditions. It was found that plasma treatment of a stainless steel plate has a significant effect on the wettability, contact angle, and free energy of the SUS304 surface. The contact angle and surface free energy were analyzed. The optimal surface modification parameters are a power of 1000 W, a torch-to-sample distance of 80 mm, a treatment time of 300 s, and an oxygen content of 1.5 wt%. Under these processing conditions, a contact angle of just 1.60° was obtained. The surface morphology, surface element composition, and surface roughness of the treated SUS304 specimens were examined using scanning electron microscopy (SEM), and atomic force microscopy (AFM), respectively. The results show that the optimal surface modification conditions lead to the formation of fine, uniformly distributed crystallites in the SUS304 microstructure. Moreover, compared to the untreated surface, the treated surface had a significantly lower carbon content and a more uniform distribution of surface peaks.