The results of film deposition of pure tungsten as well as intermetallic compound of NdFeB type on various substrates using planar ECR plasma source (with multipole magnetic field) developed in our laboratory are presented. The frequency of 2.45 GHz was generated within the magnetic system by two-slot antenna. The ions of ECR argon plasma are used for target sputtering. The main plasma parameters are density ∼1010 cm−3, Te∼15 eV, ions energy ∼20 eV, ion current density ∼3.5 mA/cm2 at the ultimate magnetron power. Under sputtering of Nd8Fe86B6 target the amorphous films with high adherence and thickness of 5 μm were formed on the substrate. The deposition rate of tungsten films (target biasing ∼900 V) was 0.59 nm/s. The fine-grained films with high adhesion were obtained. They were tested against heat loads up to 100 J/cm2 produced under irradiation of coatings with plasma streams.
Related Topics
Physical Sciences and Engineering Materials Science Surfaces, Coatings and Films
Authors
, , , , , , ,