One-step microwave calcination of ZrO2-coated TiO2 electrodes for use in dye-sensitized solar cells

TiO2 and ZrO2-coated TiO2 working electrodes were produced and calcined at 450 °C in a 2.45 GHz microwave furnace prior to incorporation in dye-sensitized solar cells. The bare TiO2 working electrodes increased from 0.2% up to 2.4% efficient after microwave calcination at a light intensity of 1 Sun. The efficiency was further increased to 3.1% for the ZrO2-coated TiO2 core-shell electrodes. The increased photovoltaic performance was due to improvements in the open circuit voltage (Voc) from 692 to 719 mV and the short circuit current density (Jsc) from 6.24 to 6.56 mA cm−2. To cite this article: David B. Menzies et al., C.R. Chimie 9 (2006).

RésuméDes électrodes de travail en TiO2 et TiO2–ZrO2, obtenues par calcination à 450 °C dans un four à micro-ondes (2,45 GHz), ont été préparées avant leur incorporation dans des cellules solaires photovoltaïques. L'efficacité des cellules solaires, soumises à une intensité lumineuse de 1 Sun, passe de 0,2 à 2,4% dans le cas des électrodes de travail constituées d'oxyde de titane. Elle atteint 3,1% avec les électrodes de travail pour lesquelles les particules de TiO2 sont recouvertes de ZrO2. Cette augmentation est due à un accroissement de la tension de circuit ouvert (Voc) de 692 à 719 mV et de la densité de courant de court-circuit de 6,24 à 6,56 mA cm−2. Pour citer cet article : David B. Menzies et al., C.R. Chimie 9 (2006).