Structural and magnetic properties of manganese zinc ferrite nanoparticles prepared by solution combustion method using mixture of fuels

The structural analysis and magnetic investigation Mn1−xZnxFe2O4 with stoichiometry (x=0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1.0) were synthesized by solution combustion method using mixture of fuel this is first of its kind. As synthesized Mn-Zn nanoferrites were characterized by X-ray Diffractometer (XRD), Transmission electron microscopy (TEM) at room temperature. The magnetic domain relaxation was investigated by inductance spectroscopy (IS) and the observed magnetic domain relaxation frequency (fr) was increased with the increase in grain size. The Room temperature magnetic properties were studied using vibrating sample magnetometer (VSM). It was observed that the real and imaginary part of permeability (μ′ and μ″), saturation magnetization (Ms), remanance magnetization (Mr) and magneton number (Mr/Ms) were decreases gradually with increasing Zn2+ concentration. The decrease in the saturation magnetization may be explained as, the Zn2+ concentration increases the relative number of ferric ions on the A sites diminishes and this reduces the A-B interaction. Hence synthesized materials are good for high frequency applications.