Abstract
The effects of magnetoelastically induced perpendicular magnetic anisotropy (PMA) on perpendicular exchange bias (PEB) have been studied in [CoO5nm/CoPt5nm]5 multilayer films. After deposition at room temperature, [CoO5nm/CoPt5nm]5 multilayer films were post-annealed at 100 °C, 250 °C, 300 °C and 375 °C for 3 h. In-plane tensile stress of CoPt layer was calculated by sin2Ï method, and we found it increased gradually upon annealing from 0.99 GPa (as-deposited) up to 3.02 GPa (300 °C-annealed). As to the magnetic property, significant enhancement of PMA was achieved in [CoO5nm/CoPt5nm]5 multilayer films after annealing due to the increase of CoPt layer in-plane tensile stress. With the enhancement of magnetoelastically induced PMA, great improvement of PEB was also achieved in [CoO5nm/CoPt5nm]5 multilayer films, which increased from 130 Oe (as-deposited) up to 1060 Oe (300 °C-annealed), showing the same change tendency as PMA and the strong correlation with CoPt layer in-plane tensile stress. We consider it is the increase of CoPt layer in-plane tensile stress that leads to the enhancement of CoPt layer PMA, which is favorable for the spins in CoPt layer aligning to a more perpendicular direction. And thus the enhanced PMA with more perpendicular spins alignment in CoPt layer results in the improved PEB in [CoO5nm/CoPt5nm]5 multilayer films through enhanced perpendicular spins coupling at CoO/CoPt interfaces.
Related Topics
Physical Sciences and Engineering
Physics and Astronomy
Condensed Matter Physics
Authors
Lei Guo, Yue Wang, Jian Wang, Shinji Muraishi, Takumi Sannomiya, Yoshio Nakamura, Ji Shi,