Samples of Fe100−xGax (x=8.3, 17.9, 20.5 and 23.3) were prepared by rapid solidification from the melt using a single Cu roller. X-ray diffraction studies of all samples showed them to be single phase with the disordered BCC structure. No evidence of superlattice reflections from D03 ordering was observed for any of the samples. Room-temperature 57Fe Mössbauer effect spectra indicated that all samples were ferromagnetically ordered. Spectra were fit to distributions of hyperfine fields. The x=8.3 sample showed a hyperfine field distribution that was single peaked and indicated a reasonably random distribution of local Fe environments. The x=17.9 and 20.5 samples showed hyperfine field distributions that were bimodal and indicated two distinct local Fe environments. The x=23.3 sample showed three distinct field components. It is suggested that the x=8.3, 17.9 and 20.5 alloys are primarily a disordered BCC phase. The x=8.3 alloy shows a small amount of short-range Ga–Ga pairing, while this short-range pairing is significantly greater in the x=17.9 and 20.5 alloys. The three field components in the x=23.3 alloy correspond well to the two sites associated with the D03 phase and a third component corresponding to a remaining L12 phase suggesting the presence of at least short-range D03 clustering in this alloy.