Effect of warm compaction on the magnetic and electrical properties of Fe-based soft magnetic composites

This paper investigates the effect of warm compaction on the magnetic and electrical properties of Fe-based soft magnetic composites at operating frequencies between 0.1 and 10 kHz. The magnetic and electrical properties of samples were measured by an LCR meter and morphology of the samples was characterized by scanning electron microscopy. It was shown that the compacted sample prepared at 800 MPa and 550 °C had the lowest magnetic loss and electrical resistivity, and highest magnetic induction and effective permeability in comparison with other samples compacted at 800 MPa and room temperature, 150, 250, 350 and 450 °C.