Nd–Fe–B-type hard phase single layer films and nanocomposite Nd28Fe66B6/Fe50Co50 multilayer films with Mo underlayers and overlayers have been fabricated on Si substrates by rf sputtering. The hysteresis loops of all films indicated simple single loops for fixed Nd–Fe–B layer thickness (10 nm) and different FeCo layer thickness (dFeCo=1–50 nm). The remanence of these films is found to increase with increasing dFeCo and the coercivity decrease with increasing dFeCo. It is shown that high remanence is achieved in the nanocomposite multilayer films consisting of the hard magnetic Nd–Fe–B-type phase and soft magnetic phase FeCo with 20 nm⩾dFeCo⩾3 nm. The sample of maximum energy product is 27 MG Oe for dFeCo=5 nm at room temperature. The enhancement of the remanence and energy products in nanocomposite multilayer films is attributed to the exchange coupling between the magnetically soft and hard phases.