The influence of the number of pulses on the morphological and photoluminescence properties of SrAl2O4:Eu2+,Dy3+ thin films prepared by pulsed laser deposition

The current work reports on the influence of the number of laser pulses on the morphological and photoluminescence properties of SrAl2O4:Eu2+,Dy3+ thin films prepared by the pulsed laser deposition (PLD) technique. Atomic force microscopy (AFM) was used to study the surface topography and morphology of the films. The AFM data showed that the film deposited using a higher number of laser pulses was packed with a uniform layer of coarse grains. In addition, the surface of this film was shown to be relatively rougher than the films deposited at a lower number of pulses. Photoluminescence (PL) data were collected using the Cary Eclipse fluorescence spectrophotometer equipped with a monochromatic xenon lamp. An intense green photoluminescence was observed at 517 nm from the films prepared using a higher number of laser pulses. Consistent with the PL data, the decay time of the film deposited using a higher number of pulses was characteristically longer than those of the other films. The effects of laser pulses on morphology, topography and photoluminescence intensity of the SrAl2O4:Eu2+,Dy3+ thin films are discussed.