Preparation and microwave–absorbing properties of NiFe2O4-polystyrene composites

NiFe2O4 nanoparticles were synthesized by the polyacrylamide gel method with acrylamide as the monomer and N,N′-methylenediacrylamide as lattice agent. The average crystallite sizes of the nickel ferrites annealed at 500, 600 and 800 °C are about 10, 30 and 50 nm, respectively. Ferrite–polystyrene composites were made by hot pressing, and microwave-absorbing properties of the composites with different contents of 35, 45, 55 and 65 wt% ferrite were investigated by testing complex permeability and complex permittivity in the X-band (8.2–12.4 GHz) frequency range. All the parameters, ε′, ε″, μ′ and μ″, increase with increasing ferrite content. The reflection losses were calculated based on a model of a single-layered plane wave absorber backed by a perfect conductor. The composite with 65 wt% ferrite content shows a minimum reflection loss of −13 dB at 11.5 GHz with a −10 dB bandwidth over the extended frequency range of 10.3–13 GHz for an absorber thickness of 2 mm.