A 5.9 tesla conduction-cooled coil composed of a stack of four single pancakes wound with YBCO wide tapes

•We made a coil composed of a stack of four single pancakes wound with YBCO wide tapes.•The coil had a central magnetic field as high as 5.9 T at 20 K.•The effect of the tape width on the central magnetic field was small near coil Ic.•We confirmed that performance of YBCO coil was improved by using wider tape.

We have been developing a conduction-cooled coil wound with YBCO-coated conductors for HTS applications. Previously, we have fabricated a coil composed of a stack of 12 single pancakes wound with 4 mm-wide YBCO tapes. This coil had a central magnetic field as high as 5.1 T at 10 K under conduction-cooled conditions. In the present study, we fabricated and tested a coil composed of a stack of four single pancakes wound with 12 mm-wide YBCO tapes. The total size of the coil and the Jc value of the tapes were almost the same as those of the former coil. At 77 K, the voltage–current characteristics showed a high n-value of 24, confirming that the coil had no degradation. Furthermore, in a conduction-cooled configuration at 20 K to 60 K, the coil showed a high n-value of over 20. At 20 K, the central magnetic field reached 5.9 T at 903 A, which is 1.3-times higher than that of the former coil.