Homoepitaxial growth of MOD-YBCO thick films on evaporated and MOD templates

We have prepared metal organic deposition (MOD)-YBCO thick films by repeating the coating-pyrolysis-crystallization procedure onto ∼100-nm-thick evaporated and MOD templates. Surface morphology of the template was found to strongly affect the homoepitaxial growth of MOD-YBCO layers on the template; namely, the epitaxial growth of MOD-YBCO on the evaporated template was much easier than that on the MOD template. A 220-nm-thick epitaxial MOD-YBCO film was successfully prepared on the 100-nm-thick evaporated-YBCO template to obtain a 320-nm-thick YBCO film, which exhibited Jc = 2.44 MA/cm2 and Ic = 78 A/cm. The Ic value has significantly increased from 37 A/cm for the evaporated-template.