Biaxially textured Ni–5 at.%W substrates have been prepared by cold rolling, followed by three different annealing routes. In this paper, the processes of melting Ni and W metals, flat rolling, various annealing methods are described in detail. The Ni–5 at.%W tapes annealed under either high vacuum or flowing Ar (7% H2) gas were characterized by X-ray pole figures, ODF, EBSD as well as AFM analysis. The texture analysis indicated that as fabricated tapes have a sharp cube texture formed after annealing at a wide temperature range of 800–1100 °C. The high quality of cube orientation on tapes was obtained after a two-step annealing (TSA), where the percentage of the cube texture component was as high as 93.5% within a misorientation angle smaller than 8° from EBSD analysis. Furthermore, it was also observed that the number of twin boundaries in this tape decreased with respect to that of tapes annealed both in vacuum and one-step gas annealing. From AFM on 1 μm2 areas, it was concluded that the roughness (RMS) on the tape surface reached 0.98 nm.