An electrochemical synthesis route for NiMnGa alloys is presented. Thin films of NiMnGa were fabricated by single step electrodeposition from aqueous electrolytes using direct current over a range of current densities. By electrolyte tuning, homogeneous films with high Ga and Mn content could be achieved at current densities as high as −400 mA cm−2. Detailed compositional analysis of the alloys showed that growth was homogeneous and oxygen content was minimized. Films plated at very low current densities were found to be nanocrystalline/amorphous. In order to obtain fully crystalline samples, thermal annealing was carried out. Mechanical characterization was assessed by nanoindentation, and the effect of Ga content on mechanical properties was investigated.