Investigations in structural morphological and optical properties of Bi-Pb-S system thin films

Bi2S3, PbS and Bi-Pb-S system thin films were grown on glass substrates by the spray pyrolysis technique. The films growth was realized by the reaction of aqueous solutions of bismuth trichloride (BiCl3) and trihydrate Lead Acetate (TLA) (Pb(CH3COO)2.3H2O) with thiourea on heated substrates. The films study was performed as a function of the TLA volume ratio (TLA vol. ratio) in the solution obtained by the mixture of BiCl3 and thiourea used as precursor solution (PrS). X-ray diffraction (XRD), field emitting scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS) were used for structural and compositional analysis of the as deposited films. With the structural investigations, Bi2S3, PbS thin films and PbS-Bi2S3 composite thin films formation was confirmed. Optical properties of the deposited films were obtained using transmittance and reflectance measurements in the wavelength range [200-2500 nm]. The absorption edge shows a shift towards low energy with the increase of the TLA vol. ratio.The optical bandgaps for the films with various TLA vol. ratio are found to lie between those of the Bi2S3 and PbS ones. The optical parameters (extinction coefficient, refractive index, real and imaginary parts if the complex dielectric constant) of the thin films are also investigated. These are found to be dependent on the TLA vol. ratio.