Controlled synthesis of various ZnO nanostructured materials by capping agents-assisted hydrothermal method for dye-sensitized solar cells

In this work, the morphology of ZnO materials could be controlled by changing the capping agent at constant alkali solution in hydrothermal process. ZnO nanomaterials with the structure of flowers, sheet-spheres and plates were obtained with the capping agent of ammonia, citric acid and oxalic acid, respectively. Thus prepared ZnO nanomaterials were characterized and applied as the photo-anode materials for dye-sensitized solar cell. All synthesized ZnO nanomaterials possessed high crystalline wurtzite structures grown in the (0 0 1) direction with the size of 2–4 μm, which consist of ZnO units around 20–400 nm. Among them, Sheet-sphere ZnO showed the highest crystallinity, surface area and uniform film morphology, resulting in the significantly improved PV performance with the overall conversion efficiency of 2.61% in dye-sensitized solar cell (DSSC) fabricated with sheet-sphere ZnO. It is notable that the ZnO materials with sphere structure may be the optimal photo-anode material among various ZnO nanomaterials for DSSC.