Synthesis and characterization of SiC nano powder with low residual carbon processed by sol–gel method

Silicon carbide nanopowders and nanowhiskers were synthesized using phenolic resin and silicon alkoxide as precursors through sol–gel process with atomic ratio of C/Si = 1.8 in water–solvent–catalyst–dispersant system. The effects of soaking time on free carbon content and synthesized β-SiC particle morphology were evaluated at 1500 °C. The synthesis process of β-SiC nanopowders was completed at 1500 °C after 1 h while β-SiC nanowhiskers were heterogeneously nucleated and grown from obtained nanopowders after 2–3 h. The detected free carbon content in whiskers was less than 1% after 3 h.

Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Mixing of the precursors in the molecular scale by sol-gel processing. ► Producing of β-SiC nano particles with residual carbon contents lower than 1%. ► Obtaining SiC/SiO2 nano composite using sol-gel method. ► Synthesis of β-SiC nano whiskers with diameter about 60 nm and length about 10 μm.