Tritium release from neutron-irradiated Li2O: Transport in porous sintered pellets

The tritium release behavior from Li2O sintered pellets (81–88% T.D.) is examined by isothermal heating tests. (1) For the 88% T.D. specimens, the fraction of residual tritium is found to follow the square-root law of the annealing time. The rate-determining process is the migration in the connected micro-pore. (2) For the 81% T.D. specimens, which are annealed after irradiation at 630 K for 4 h, the fraction of residual tritium is also found to follow the square-root law of the annealing time. The rate-determining process is the migration in the connected micro-pore. (3) For the 81% T.D. specimens as irradiated, the tritium release rate is found to follow the square-root law of the annealing time. The rate-determining process is controlled by Kohlrauch stretched exponential form. Tritium trapped in irradiation defects released with recovering the defects by isothermal heating.