Surface self-magnetization of siderite is achieved by generating ferromagnetic substance on the surface of siderite by adjusting slurry temperature, pH value, stirring rate and reaction time. No addition of any iron-containing reagent is required. The temperature of 60 °C, NaOH concentration of 0.10 mol/L; stirring rate of 900 r/min and the reaction time of 10 min are the optimal conditions. The results show that the siderite recovery in magnetic separation increased from 26.9% to 88.8% after surface magnetization. Magnetization kinetic equation is expressed as 1 − [1 − (ɛ − 0.269)]1/3 = Kt. Activation energy for the magnetization reaction is 4.30 kJ/mol. VSM, SEM and XPS were used to characterize the siderite, and results show that the saturated magnetization (σs) of siderite increased from 0.652 to 2.569 A m2/kg, the magnetic hysteresis was detected with a coercive force of 0.976 A/m after magnetization; Fe2P3/2 electron binding energy changed which reflects the valence alteration in iron on the surface and the formation of ferromagnetic Fe3O4.