Determination of mixed-mode stress intensity factors, fracture toughness, and crack turning angle for anisotropic foam material

A numerical and experimental investigation for determining mixed-mode stress intensity factors, fracture toughness, and crack turning angle for BX-265 foam insulation material, used by NASA to insulate the external tank (ET) for the space shuttle, is presented. BX-265 foam is a type of spray-on foam insulation (SOFI), similar to the material used to insulate attics in residential construction. This cellular material is a good insulator and is very lightweight. Breakup of segments of this foam insulation on the shuttle ET impacting the shuttle thermal protection tiles during liftoff is believed to have caused the space shuttle Columbia failure during re-entry. NASA engineers are interested in understanding the processes that govern the breakup/fracture of this material from the shuttle ET. The foam is anisotropic in nature and the required stress and fracture mechanics analysis must include the effects of the direction dependence on material properties. Material testing at NASA Marshall Space Flight Center (MSFC) has indicated that the foam can be modeled as a transversely isotropic material. As a first step toward understanding the fracture mechanics of this material, we present a general theoretical and numerical framework for computing stress intensity factors (SIFs), under mixed-mode loading conditions, taking into account the material anisotropy. We present SIFs for middle tension – M(T) – test specimens, using 3D finite element stress analysis (ANSYS) and FRANC3D fracture analysis software. SIF values are presented for a range of foam material orientations. Mode I fracture toughness of the material is determined based on the SIF value at failure load. We also present crack turning angles for anisotropic foam material under mixed-mode loading. The results represent a quantitative basis for evaluating the strength and fracture properties of anisotropic foam insulation material.