Low cycle fatigue behaviors of elbow pipe with local wall thinning

Low cycle fatigue tests were conducted using 100A elbow specimens made of STPT410 carbon steel with local wall thinning. Local wall thinning by erosion/corrosion was simulated by machined pipe wall thinning. The local wall thinning areas were located at three different areas, called extrados, crown and intrados. The elbow specimens were subjected to cyclic in-plane bending under displacement control without internal pressure. The effects of eroded conditions, such as eroded ratio, eroded angle and position, on the low cycle fatigue behavior and fatigue life were discussed by using experimental results and finite element analyses. Also the location of crack initiation and the crack growth direction could be predicted by three dimensional elasto-plastic finite element analyses. In addition, the safety margin of eroded elbows against seismic loading was discussed by comparing the fictitious stress of elbows with the allowable stress limit demanded by the design code.