3160772 Journal of Prosthodontic Research 2009 4 Pages PDF
Abstract

PurposeThe purpose of this study was to examine the bond strength between tooth-colored porcelain and sandblasted zirconia framework.MethodsThe surfaces of zirconia specimens that had been cut into a size suitable for a bending test were sandblasted at three different pressures (0.2, 0.4 and 0.6 MPa). The surface roughness of each specimen was measured and then a 3-point bending test was performed. After that, other zirconia specimens simulating a crown framework were fabricated and their surfaces were sandblasted. Three types of tooth-colored porcelain were fired onto the surface of those zirconia specimens, and the tensile bond strength between the two substances was examined.ResultsWhen the sandblasting pressure was increased, the surface roughness of zirconia specimens tended to become, but the flexural strength remained unchanged. The specimens simulating a zirconia framework had a higher strength of bond when sandblasted at 0.4 or 0.6 MPa than when blasted at 0.2 MPa. The zirconia specimens sandblasted at a pressure of 0.4 MPa had a bond strength to tooth-colored porcelain of 37.7–49.5 MPa.ConclusionWhen sandblasted at a pressure of 0.4 MPa, the zirconia specimens developed a strong bond with the tooth-colored porcelain, regardless of the type of porcelain.

Related Topics
Health Sciences Medicine and Dentistry Dentistry, Oral Surgery and Medicine
Authors
, , , , , ,